The SPEED WELD Process is most suitable for joining components of thin to thick wall thicknesses. Good penetration depths and perfect side wall joints at high weld speeds are achieved by means of a focused pulsed arc with a scalable deposition rate. The SPEED WELD Process is used in all industrial production sectors.
| Technical Data | Fillet weld | Overlap weld |
| Material | 1.4316 | 1.4316 |
| Wire Ø, mm | 1,0 | 1,0 |
| Wire feed VD , m/min | 5,8 | 5,0 |
| Weld speed Vs, cm/min | 80 | 70 |
| Voltage U, V | 21,0 | 21,0 |
| Current I, A | 130 | 130 |
| Plate thickness, mm | 1,5 / 1,5 | 1,5 / 1,5 |
Suitable power sources
- QINEO® PULSE
- QINEO® CHAMP
Applications
- Thin to thick materials
- Mainly automated welding, but also manual welding
Advantages
- Good penetration depths at high weld speeds
- Perfect side wall joints
- High-quality weld seams
Material
- Steel
- High-strength steel
- Aluminum
- Chrome nickel materials
- Coated plates